About: Carbon Fiber Nylon/CF-PA, A brief introduction.
CF-PA is based on nylon 6/66 copolymer, adding 20% carbon fiber greatly enhances the strength, rigidity and toughness of nylon, and can replace metal materials in many occasions; Self-lubricating wear resistance makes it suitable for printing gears; High toughness and impact resistance make it suitable for printing durable parts. High temperature resistance, heat deformation temperature up to 155℃; Low shrinkage, it is not easy to warp and crack when printing, and the surface of printed models is matte and delicate.
Sellingpoint
Heat resistance
High-intensity
High rigidity
High toughness
High impact resistance
| Filament Properties Table | |
|---|---|
| 3D PRINTING FILAMENT | ePA-CF |
| Density(g/cm3) | 1.24 |
| Heat Distortion Temp(℃,0.45MPa) | 155 |
| Melt Flow Index(g/10min) | 11.46(275℃/5kg） |
| Tensile Strength(MPa) | 140 |
| Elongation at Break(%) | 10.61 |
| Flexural Strength(MPa) | 140 |
| Flexural Modulus(MPa) | 4363 |
| IZOD Impact Strength(kJ/㎡) | 18.67 |
| Durability | 10/10 |
| Printability | 8/10 |
| Recommended printing parameters | |
| Extruder Temperature(℃) | 260 – 300℃ Recommended temperature：280℃ |
| Bed temperature(℃) | 45 – 60°C |
| Fan Speed | 0% |
| Printing Speed | 40 – 100mm/s |
| Heated Bed | Optional |
| Recommended Build Surfaces | Masking paper, PVP solid glue, PEI |
| Feature | |
| Flexible | —— |
| Elastic | —— |
| Impact Resistant | √ |
| Soft | —— |
| Composite | √ |
| UV Resistant | —— |
| Water Resistant | —— |
| Dissolvable | —— |
| Heat Resistant | √ |
| Chemically Resistant | —— |
| Fatigue Resistant | —— |
| Need drying | √ |
| Heated Bed Required | —— |
| Print recommend | Drying at 70℃/>12h, using hardened steel, ruby nozzle |
Abrasive resistance
High dimensional stability
Matte surface effect
Excellent printability